Shell Alvania G3 Data Sheet [updated] -

: Fortified with anti-rust additives to protect metal surfaces in hostile or humid environments. Water Resistance

Avoid mixing with polyurea, clay (bentonite), or calcium sulfonate greases. Mixing with other lithium greases (same base oil type) is generally acceptable but not optimal. Always purge old grease completely. shell alvania g3 data sheet

The grease contains oxidation inhibitors that prevent the oil from thickening or forming sludge during prolonged exposure to high temperatures. This extends the re-lubrication intervals and bearing life. : Fortified with anti-rust additives to protect metal

| Parameter | Typical Value | Test Method | |-----------|---------------|--------------| | | 3 | ASTM D217 | | Thickener Type | Lithium hydroxystearate | - | | Base Oil Viscosity @ 40°C | 100 – 130 mm²/s (cSt) | ASTM D445 | | Base Oil Viscosity @ 100°C | 11 – 12 mm²/s (cSt) | ASTM D445 | | Dropping Point | > 190°C (374°F) | ASTM D566 | | Worked Penetration @ 25°C (60 strokes) | 220 – 250 (0.1 mm) | ASTM D217 | | Unworked Penetration | 230 – 260 (0.1 mm) | ASTM D217 | | Roll Stability (penetration change after 72h) | Max +30 points | ASTM D1831 | | Water Washout @ 79°C | < 5% weight loss | ASTM D1264 | | Copper Corrosion (24h @ 100°C) | 1b (slight tarnish) | ASTM D4048 | | Rust Prevention (SKF EMCOR test) | Pass – Rating 0,0 | ASTM D6138 | | Oil Separation (7 days @ 40°C) | < 5% | ASTM D1742 | | Operating Temperature Range | -20°C to +130°C (-4°F to +266°F) Intermittent peaks up to +150°C | - | | Four-Ball Weld Load (scar diameter) | > 300 kg | ASTM D2596 | | Four-Ball Wear Scar (1h @ 40kg) | < 0.5 mm | ASTM D2266 | Always purge old grease completely